FOSTER ® MONOLAR ® COATING FOSTER MONOLAR Coating is a tough flexible fire-resistive elastomeric finish for protection of outdoor thermal insulation. It contains chlorosulfonated polyethylene rubber (formerly known as Hypalon ® *). It is an excellent vapor barrier for low temperature


Category: commercial insulation | cryogenic coatings | plumbing insulation...

MasterFormat: Thermal Protection | Fire-Retardant Coatings | Elastomeric Coatings...


Related Products

Overview


Foster® 60-95 / 60-96 MONOLAR® COATING



FOSTER ® MONOLAR ® COATING

FOSTER MONOLAR Coating is a tough flexible fire-resistive elastomeric finish for protection of outdoor thermal insulation. It contains chlorosulfonated polyethylene rubber (formerly known as Hypalon ® *). It is an excellent vapor barrier for low temperature insulation on tanks, pipework, vessels, ductwork, and fittings.

MONOLAR Coating provides outstanding weather barrier protection, showing good color retention, excellent chemical resistance, and durability. It has excellent resistance to UV and sunlight.

MONOLAR Coating provides outstanding weather barrier and vapor barrier protection for sprayed polyurethane foam in outdoor locations. It is a one-component, high film strength product, usually applied in two coats with standard airless spray equipment. It sprays easily and cleanly with a minimum of cobwebbing.

MONOLAR Coating is an ideal finish for flexible cellular insulation tubing and sheets. Apply by brush in two coats.

MONOLAR Coating is produced under the classification and follow-up service of Underwriter's Laboratories, Inc.

MONOLAR Coating meets NFPA 90A and 90B 25/50 requirements.

MONOLAR Coating contains no asbestos, lead, mercury, or mercury compounds.

LIMITATIONS
Store and apply between 40ºF (4ºC) and 100ºF (38ºC). For best results, select ElastolarTM 95-44 for insulation joint sealing under Monolar coating. Always test plastic materials for compatibility when using a solvent base product. Outdoor horizontal surfaces must always drain completely. A pitch of at least 1/2" per foot (4 cm/m) is recommended. Make certain this product is completely dry and the area free from solvent odor if food is involved. Select Monolar Mastic 60-90 (white) or 60-91 (gray) for trowel or glove application. * Chlorosulfonated polyethylene rubber is also known as Hypalon, a trademark of Dupont Performance Elastomers, and is no longer produced by Dupont.


COLOR:
60-95 White 60-96 Gray Other colors available on special order.

APPLICATION CONSISTENCY:
Airless spray or brush

AVERAGE WEIGHT / U.S. GALLON (ASTM D 1475):
9.5 to 9.9 lbs. (1.14 to 1.19 kg/l)

AVERAGE NON-VOLATILE (ASTM D 1644):
33% by volume (46% by weight)

COVERAGE RANGE (FSTM 72):
(Subject to the nature of material coated.) Wet coverages shown below are for smooth non-porous surfaces. Porous or rough surfaces will require higher gallonage to attain required dry thickness.
Dry Thickness: 0.032 inch (0.8 mm) Equivalent Wet Coverage: 0.096 inch (2.4 mm) 6 gal./100 sq. ft. (2.4 l/m2 )

DRYING TIME (ASTM D 1640):
Set to Touch: 3-4 hours
Dry Through: 24 hours

SERVICE TEMPERATURE LIMITS (FSTM 70):
(Temperature at coated surface) -50ºF to 220ºF (-46ºC to 104ºC)

WATER VAPOR PERMEANCE:
ASTM E 96, Method E, 0.025 perms (0.016 metric perms) at 51 mils dry (1.3mm) ASTM E-96 Procedure A, 0.018 perms (0.012 metric perms) at 26 mils (0.66mm) dry ASTM F 1249, 0.05 perms (0.033 metric perms) at 30 mils dry (0.8mm). Tested at 100ºF (38ºC) and 90% RH.

WET FLAMMABILITY (ASTM D 3278):
Flash point 110ºF (43ºC)

SURFACE BURNING CHARACTERISTICS

(ASTM E 84):
Flame Spread: 10
Smoke Developed: 15
Tested at coverage rate of 25 sq. ft./gal. (0.61 m2 /l).
Applied to 1/4 inch (6.4mm) inorganic reinforced cement board. The flame spread may vary at different product thicknesses and/or when applied over other surfaces.