Tnemec Company Inc. -Series 27WB Typoxy - Inorganic Hybrid Water-Based Epoxy

DOWNLOADS

Generic Type

Inorganic Hybrid Water-Based Epoxy

Common Usage

A unique, low odor, low VOC, water-based epoxy coating featuring HydroLink curing technology for exceptional durability and corrosion resistance.


Category: factory-applied coatings for metal | shop applied coatings | shop-applied coatings for metal...

MasterFormat: Cast-In-Place Concrete | Concrete Finishing | Common Work Results for Metals...



Tnemec Company Inc.
6800 Corporate Drive
Kansas City, MO 64120
Tel: (816) 326-4264

ist@tnemec.com

https://www.tnemec.com/

Find a rep/distributor

Request More Info

DOWNLOADS

Related Products

Overview


Series 27WB Typoxy - Inorganic Hybrid Water-Based Epoxy

Generic Type

Inorganic Hybrid Water-Based Epoxy

Common Usage

A unique, low odor, low VOC, water-based epoxy coating featuring HydroLink curing technology for exceptional durability and corrosion resistance. Used for the protection and finishing of steel and concrete structures including structural steel, tanks, pipes, and equipment. Superior wetting for marginally prepared steel and tightly adhered existing coatings. This coating is ideally suited for steel fabrication and OEM applications, with fast-curing and rapid handling properties. Series 27WB exhibits low yellowing and good color stability in whites and light tone colors. Formula protected under U.S. patent.

Theoretical Coverage

1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates. †

Primers

Steel: Self-priming or Series 1, 66, 66HS, L69, L69F, N69, N69F, 90G-1K97, 90-97, H90-97, 91-H²O, 94-H²O, 161, 161HS, 394. Note: Series 1, 90G-1K97, 90-97, H90-97, 91-H²O, 94-H²O and 394 must be exterior exposed for 24 hours prior to topcoating.
Galvanized Steel: Self-priming
Concrete: Self-priming, 215, 217, 218, 1254
CMU: Self-priming, 130, 215, 1254
Drywall: Self-priming, 151

Finish

Satin

Curing Time

Temperature - To Touch - To Handle - To Recoat†

120°F (49°C) - 15 minutes - 1 hour - 2 hours

95°F (35°C) - 30 minutes - 2 hours - 3 hours

75°F (24°C) - 1 hour - 6 hours - 8 hours

55°F (13°C) - 2 hours - 8 hours - 16 hours

45°F (7°C) - 3 hours - 10 hours - 24 hours

35°F (2°C) - 4 hours - 3 days - 4 days

Curing time varies with surface temperature, air movement, humidity and film thickness. For immersion service cure a minimum of 24 hours at 75°F (24°C). The following minimum recoat times apply when topcoating with Series 297, 1080 or 1081: 95°F (35°C) 12 hours, 75°F (24°C) and 55°F (13°C) 24 hours, 45°F (7°C) 4 days, 35°F (2°C) 7 days. Note: For faster cure in temperatures down to 35°F (2°C), add No. 44-700 Epoxy Accelerator, see separate product data sheet for cure information. Note: The use of Series 44-700 Accelerator is not recommended when temperatures exceed 75°F (24°C).

HAPS

0 lbs/gal solids

Number of Components

Two: Part A and Part B (One Part A to One Part B by volume.)

Volume Solids

100% (mixed) †

Recommended DFT

3.0 to 14.0 mils (75 to 350 microns) per coat. Note: Number of coats and thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.

Volatile Organic Compounds

Unthinned: 0.01 lbs/gallon (0.9 grams/litre) †

Topcoats

Series 30, 66HS, 72, 73, 113, 114, 115, 156, 157, 158, 161HS, 180, 181, 270, 273, 280, 281, 287, 290, 291, 297•, 406, 435, 436, 446, 740, 750, 1026, 1028, 1029, 1070, 1070V, 1071, 1071V, 1072, 1072V, 1074, 1074U, 1075, 1075U, 1077, 1078, 1080•, 1081•. Note: When topcoating with Series 740 or 750 over 27WB, a 90 day maximum recoat time applies. •An extended cure time is needed when topcoating with Series 297, 1080 or 1081. Reference additional recoat times listed below the cure table. Note: More than one finish coat may be required to achieve uniform and desired gloss level.