Tnemec Company Inc. -Series 208 Epoxoprime MVT - Modified Polyamine Epoxy

DOWNLOADS

Generic Type

Modified Polyamine Epoxy

Common Usage

Epoxoprime MVT is a unique, moisture-tolerant, two component, low viscosity, high solids epoxy primer designed to reduce moisture vapor emissions


Category: alkali-resistant coatings | finishes | high-performance coatings...

MasterFormat: Cast-In-Place Concrete | Concrete Finishing | Flooring...



Tnemec Company Inc.
6800 Corporate Drive
Kansas City, MO 64120
Tel: (816) 326-4264

ist@tnemec.com

https://www.tnemec.com/

Find a rep/distributor

Request More Info

DOWNLOADS

Related Products

Overview


Series 208 Epoxoprime MVT - Modified Polyamine Epoxy

Generic Type

Modified Polyamine Epoxy

Common Usage

Epoxoprime MVT is a unique, moisture-tolerant, two component, low viscosity, high solids epoxy primer designed to reduce moisture vapor emissions and provide alkalinity control for concrete with elevated moisture vapor transmission levels that exceed the acceptable limits of non-breathing resilient and polymer floor topping finishes. Epoxoprime MVT can be applied to properly prepared, 10 day old concrete and withstands moisture vapor transmission up to 15 lbs (per ASTM F 1869) and relative humidity up to 95% (per ASTM F 2170). Epoxoprime MVT has a low perm rating (0.05 perm) and is alkaline insensitive to pH levels of 14.

Topcoats

Series 201, 205, 206, 206SC, 210, 222, 223, 224, 233, 237, 237SC, 238, 239, 239SC, 247, 248, 280, 280FC, 281, 282, 290, 291, 294, 295, 296, 297. Note: Refer to the applicable topcoat data sheet for color availability and additional information. Note: If Series 247 (tinted), 248 (tinted), 290, 291 or 297 is selected for the finish coat, Series 208 must be tinted or a tinted intermediate coat must be utilized.

Volatile Organic Compounds

0.09 lbs/gallon (11 grams/litre)

Theoretical Coverage

1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates.

Curing Time

Temperature - To Topcoat - Max Recoat

75°F (24°C) - 6-8 hours - 24 hours

Note: If more than 24 hours have elapsed between coats, the coated surface must be mechanically abraded before topcoating. Note: If Series 208 is used as the primer for an epoxy mortar system, the 208 primer must be reprimed with Series 201 or 237 prior to placing the mortar. The mortar application should take place while the Series 201 or 237 is still tacky, typically up to four hours, otherwise, aggregate should be lightly broadcast into the 201 or 237 primer while wet so to provide anchor points for the trowel application. Do not broadcast aggregate into the Series 208 Epoxoprime MVT.

Number of Components

Two: Part A and Part B (2 Parts A to 1 Part B by volume)

HAPS

0.0 lbs/gal solids

Volume Solids

100% (mixed)

Recommended DFT

16.0 to 20.0 mils (406 to 508 microns) per coat. Note: The potential for outgassing increases with higher film thickness. Care should be taken during application to reduce these occurrences. Reference the application section of this product datasheet for important information on environmental requirements.

Surfacer/Filler/Patcher

Series 208 mixed with fumed silica may be used for small patches or crack repairs. Certain high-early strength, cementious repair mortars are also acceptable for deeper filling and patching. Contact Tnemec for further qualifications.


See More